Loctite® Fixmaster® 235611 Flex 80™ 2-Part Pourable Repair Compound Putty, 6 lb Kit, Liquid Form, Black Part A, Brown Part B, 1.07 Part B
- Manufacturers: Henkel
- Brand Name: Loctite®
- PN: LOC97422
- MPN: 235611
- UPC: 079340974227
- Min. Order Qty: 1
- Qty. Interval: 1
DESCRIPTION
Loctite® Fixmaster® Repair Compound Putty, 2-Part Pourable, Series: Flex 80™, Kit Container, 6 lb Container, Polyurethane Base, Composition: Part A: Di(2-Ethylhexyl)Phthalate, Diethylmethylbenzenediamine and Carbon Black, Part B: Polyurethane Pre-Polymer Dicyclohexylmethane-4,4'-DiIsocyanate, Methylenebis(Phenyl Isocyanate, Polymeric Diphenylmethane DiIsocyanate, Liquid Form, 604 sq-cm at 6 mm THK/0.45 kg Coverage, 10 min Application Time, 8 hr at 25 deg C Curing, Black Part A, Brown Part B, Aromatic Odor/Scent, -29 to 82 deg C, 1.07 Part B Specific Gravity, Part A: 163 deg C, Part B: > 162.77 deg C Flash Point, 100:40 By Volume/72:28 By Weight Mixing Ratio, Applicable Materials: Rubber, 1500 psi Tensile Strength, 480 psi Shear Strength
SPECIFICATIONS
Applicable Materials : Rubber
Application Time : 10 min
Base Type : Polyurethane
Composition : Part A: Di(2-Ethylhexyl)Phthalate, Diethylmethylbenzenediamine and Carbon Black, Part B: Polyurethane Pre-Polymer Dicyclohexylmethane-4,4'-DiIsocyanate, Methylenebis(Phenyl Isocyanate, Polymeric Diphenylmethane DiIsocyanate
Coverage : 604 sq-cm at 6 mm THK/0.45 kg
Curing Time : 8 hr at 25 deg C
Flash Point : Part A: 163 deg C, Part B: > 162.77 deg C
Mixing Ratio : 100:40 By Volume/72:28 By Weight
Odor/Scent : Aromatic
Series : Flex 80™
Shear Strength : 480 psi
Temperature Rating : -29 to 82 deg C
Tensile Strength : 1500 psi
Type : 2-Part Pourable
Container Size : 6 lb
Container Type : Kit
Form : Liquid
Color : Black Part A, Brown Part B
Specific Gravity : 1.07 Part B
FEATURES
Pourable repair compound is a trowelable, two-part urethane
Easy to mix and use
Unaffected by oil, grease and water
Provides impact, abrasion, and corrosion-resistant protection
A 87 shore hardness
10 to 15 min gel time 21 deg C
Polyurethane hardener part A, polyurethane adhesive part B